NiFe2-xBixO4 (x = 0, 0.1, 0.2, 0.3) nanoparticles with various grain sizes were synthesized via annealing treatment followed by ball milling of its bulk component materials. Commercially available bismuth, nickel and iron oxide powders were first mixed and then annealed at 1200 _C in an oxygen environment furnace for 4 h. The samples were then milled for 2 h by high-energy ball milling. X-ray diffraction (XRD) pattern indicated that in this stage the samples are single phase. The microstructure investigation was carried out by a scanning electron microscope with maximum magnification of 30,000. The average grain size for different samples was estimated by XRD technique and transmission electron microscopy. Magnetic behavior of the samples at room temperature was studied using an alternating gradient force magnetometry. The Ne´el temperature of the powders was measured by a Faraday balance. Based on magnetic studies, increase in bismuth content leads to a decrease in the saturation magnetization, coercive field and Ne´el temperature. This can be attributed to the substitution of Bi3? ion in the ferrite system as a nonmagnetic cation.
|